聚氨酯弹性体/纤维素纳米晶体复合材料的制备及性能研究

Preparation and property of polyurethane elastomer/CNC composite
收藏 分享 导出
摘要 通过浓硫酸水解脱脂棉制备纤维素纳米晶体(CNC),并用3-氨基丙基三乙氧基硅烷(APTS)对其进行表面修饰。以4,4-二苯基甲烷二异氰酸酯(MDI)、聚四氢呋喃(PTMG)、CNC、1,4-丁二醇(BD)为原料制备聚氨酯弹性体/纤维素纳米晶体(PUE/CNC)复合材料,研究了CNC用量对PUE/CNC复合材料性能的影响。结果表明:当CNC用量达到1%(wt,质量分数,下同)时,复合材料的拉伸强度和断裂伸长率分别提高了178%和97.5%,热性能也有所提高;但CNC用量超过1.5%后,复合材料的力学性能下降,热性能仍保持提升。 Cellulose nanocrystals(CNC)were prepared by hydrolysis of absorbent cotton by concentrated sulfuric acid and surface modified with 3-aminopropyltriethoxysilane(APTS).Then use 4,4-diphenylmethane diisocyanate(MDI),poly(tetramethlene glycol)(PTMG),CNC,and 1,4-butanediol(BD)as raw materials,polyurethane elastomer/cellulose nanocrystal(PUE/CNC)composites were prepared.The influence of the amount of CNC on the properties of the composite was studied.The results shown that when the amount of CNC reached 1wt%,the tensile strength and elongation at break of the composites were increased by 178%and 97.5%,respectively,and the thermal properties are also improved.However,when the amount of CNC exceeded 1.5wt%,the mechanical properties of the composites decreased,and the thermal properties remained elevated.
作者 马加佳 谢明圣 田秀枝 蒋学 王鸿博 高卫东 Ma Jiajia;Xie Mingsheng;Tian Xiuzhi;Jiang Xue;Wang Hongbo;Gao Weidong(Key Laboratory of Ecological Textiles,Ministry of Education,School of Textiles and Clothing,Jiangnan University,Wuxi 214122;Jiangsu Functional Textile Engineering Technology Research Center,Wuxi 214122)
出处 《化工新型材料》 CAS CSCD 北大核心 2019年第10期83-87,共5页 New Chemical Materials
基金 国家自然科学基金(31570578,31270632) 教育部中央高校基本科研业务费专项资金(JUSRP51622A)。
关键词 纤维素纳米晶体 聚氨酯 复合材料 力学性能 热性能 cellulose nanocrystal polyurethane composite mechanical property thermal property
作者简介 马加佳(1994-),男,硕士,研究方向为功能高分子材料;联系人:蒋学(1976-),男,教授,主要从事纤维素纳米晶体的制备及其应用研究。