Ti含量对脱氧剂45%Al-Fe-3%RE合金铸态组织与硬度的影响 预览

Influence of Ti Addition on As-Cast Structure and Hardness of Deoxidizer 45%Al-Fe-3%RE Alloy
在线阅读 下载PDF
收藏 分享 导出
摘要 采用中频感应真空熔炼炉制备含Ti的脱氧剂45%Al-Fe-3%RE合金,并借助X射线、扫描电镜、能谱分析和硬度检测仪对合金铸态组织及硬度进行分析。结果表明,随着Ti含量(0,0.2%,0.3%,0.4%,0.5%)的增加,合金中的铸态组织晶粒得到明显的细化,并且组织更加致密;当Ti含量为0.3%时,合金的硬度最大,硬度值为HV 95。 45%Al-Fe-3%RE alloy containing Ti was prepared using a vacuum medium frequency induction melting furnace. The as-cast structure and the hardness of 45%Al-Fe-3%RE alloy was analyzed by X-ray diffraction,SEM, spectroscopy and hardness tester. The results show that the grains in the as-cast structure of the alloy are significantly refined and the structure is more compact with increasing Ti content(0, 0.2%, 0.3%, 0.4%, 0.5%)in the 45%Al-Fe-3%RE alloy. When Ti content is 0.3%, the hardness of the alloy is the maximum, with a hardness value of HV 95.
作者 范秀风 闫永旺 陈义胜 宋巍 FAN Xiu-feng;YAN Yong-wang;CHEN Yi-sheng;SONG Wei(Analytical and Testing Center, Inner Mongolia University of Science and Technology, Baotou 014010, Inner Mongolia, China;Material and Metallurgy School, Inner Mongolia University of Science and Technology, Baotou 014010, Inner Mongolia, China)
出处 《铸造》 CAS 北大核心 2019年第3期254-257,共4页 Foundry
基金 内蒙古自治区高等学校科学研究项目(NJZY17170) 内蒙古自然科学基金项目(2017MS0533) 内蒙古科技大学创新基金科研启动项目(2014QDL050)。
关键词 脱氧剂 45%Al-Fe-3%RE合金 铸态组织 硬度 deoxidizer 45%Al-Fe-3%RE alloy as-cast structure hardness
作者简介 范秀风(1973-),女,讲师,研究生,研究方向为稀土功能材料。电话:0472-5288192,E-mail:fxf_tt@163.com;通讯作者:闫永旺,男,副教授。E-mail:yanyongwang88@163.com.
  • 相关文献

参考文献17

二级参考文献129

共引文献48

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈