内养护对不同细度水泥制备的砂浆性能的影响 被引量:6

Influence of Internal Curing on Properties of Cement Mortars Prepared from Different Fineness Cements
收藏 分享 导出
摘要 研究了饱和轻骨料内养护对不同细度水泥配制的砂浆自收缩、强度、水化程度、显微硬度以及界面过渡区形貌等的影响。结果发现:内养护可显著降低不同细度水泥配制的砂浆的早期自收缩,但减缩效果随着水泥比表面积增大而降低;内养护的砂浆后期自收缩仍持续增加,水泥越粗,自收缩后期增长越大;内养护能够显著促进水泥早期水化,这种促进作用在细水泥中最显著。在相同条件下,轻骨料的引入对砂浆强度的影响作用与水泥细度有关;显微硬度以及界面过渡区微观形貌结果显示,轻骨料内养护能显著改善粗水泥体系微观结构,对细水泥体系微观结构的改善则无显著贡献。 The influence of internal curing(IC) with pre-saturated light weight aggregate(LWA) on the properties of cement mortars prepared from three different finenesses cements was investigated.The corresponding experiments for the autogenous shrinkage,strength,hydration degree,microhardness and microstructures of interfacial transition zone(ITZ) were conducted.It was shown that the IC could reduce the early-age autogenous shrinkage of cement mortars,and the finer cement could give the lower shrinkage re-duction.Nonetheless,the long-term autogenous shrinkage of internally cured cement mortars had a considerable development,espe-cially for mortar with the coarser cement.The IC could promote the hydration of cement at early age,and the promotion was more significant for the finer cement.The effect of IC on the compressive strength of mortar was correlated to the cement fineness under the same internal curing condition.In addition,the results of microhardness and ITZ microstructure of cement pastes indicated that the IC-LWA could favor the improvement of microstructures for the coarser cement systems,but it could not have any the improve-ment for the finer ones.
作者 党玉栋 钱觉时 曲艳召 郭清春 贾兴文 王智 DANG Yudong,QIAN Jueshi,QU Yanzhao,GUO Qingchun,JIA Xingwen,WANG Zhi(1.College of Materials Science and Engineering,Chongqing University,Chongqing 400045,China;2.College of Chemistry and Chemical Engineering,Chongqing University,Chongqing 400044,China)
出处 《硅酸盐学报》 EI CAS CSCD 北大核心 2012年第5期 657-663,共7页 Journal of The Chinese Ceramic Society
基金 西部交通科技项目(2009318000033) 高性能土木工程材料国家重点实验室开放基金(2010CEM011)项目资助
关键词 水泥细度 内养护 轻骨料 砂浆 自收缩 cement fineness internal curing light weight aggregate cement mortar autogenous shrinkage
作者简介 党玉栋(1983-),男,博士研究生。 通信作者:钱觉时(1962-),男,博士,教授。
  • 相关文献

参考文献25

  • 1TOYOHARU N, TOMOAKI H. Autogenous shrinkage of high-per-formance concrete [C]// Proceeding of the International Workshop on Microstructure and Durability to Predict Service Life of Concrete Structures, Japan: FEB, 2004: 86-95. 被引量:1
  • 2TAZAWA E, KONKURITO KOGAKU KYOKAI N. Autogenous shrinkage of concrete [M]. Hiroshima: Taylor & Francis, 1999: 13-14. 被引量:1
  • 3BENTZ D P, JENSEN O M. Mitigation strategies for autogenous shrinkage cracking [J]. Cem Concr Compos, 2004, 26(6): 677-685. 被引量:1
  • 4JENSEN O M, HANSEN P F. Water-entrained cement-based materials I. Principles and theoretical background [J]. Cem Concr Res, 2001, 31 (4): 647-654. 被引量:1
  • 5HENKENSIEFKEN R, BRIATKA P, NANTUNG T, et al. Plastic shrinkage cracking in internally cured mixtures made with pre-wetted lightweight aggregate [J]. Concr Int, 2010, 32(2): 49-54. 被引量:1
  • 6CUSSON D, LOUNIS Z, DAIGLE L. Benefits of internal curing on service life and life-cycle cost of high-performance concrete bridge decks-A case study [J]. Cem Concr Comp, 2010, 32(5): 339-350. 被引量:1
  • 7BENTZ D E Influence of internal curing using lightweight aggregates on interracial transition zone percolation and chloride ingress in mortars [J]. Cem Concr Comp, 2009, 31(5): 285 289. 被引量:1
  • 8CHLITTER J, HENKENSIEFKEN R, CASTRO J, et al. Development of internally cured concrete for increased service life [R]. FHWA/IN/ JTRP-2010/10. West Lafayette: Purdue University, 2010. 被引量:1
  • 9VILLAREAL V. Internal curingreal world ready mix production and applications: a practical approach to lightweight modified concrete [C]// BENTZ D P, MOHR Bed. Internal Curing of High-Performance Concrete: Laboratory and Field Experiences. Farmington Hills: American ConcreteInstitute, 2008: 45-56. 被引量:1
  • 10FRIGGLE T, REEVES D. Internal curing of concrete paving: laboratory and field experience [C]//BENTZ D P, MOHR Bed. Internal Curing of High-Performance Concrete: Laboratory and Field Experiences. Farmington Hills: American Concrete Institute, 2008: 71-80. 被引量:1

二级参考文献42

  • 1董淑慧,张宝生,葛勇,袁杰.轻骨料对混凝土自养护减缩效率的影响[J].硅酸盐学报,2009(3):465-469. 被引量:24
  • 2胡曙光,王发洲,丁庆军.轻集料与水泥石的界面结构[J].硅酸盐学报,2005,33(6):713-717. 被引量:42
  • 3LUO Jiying,LENG Faguang,FENG Naiqian,et al.The effect of qantity of fly ash on the strength and durability of high-performance concrete[J].China Build Mater Sci Technol (in Chinese),2001,(3):15-18. 被引量:1
  • 4GUO Xiaoyan,WANG Fuchuan,NAN Fang.Study on the high performance concrete with high content of fly ash[J].J Build Mater (in Chinese),1998,(6):93--96. 被引量:1
  • 5ZHEN Y.Application of fly ash in dam concrete[A]//Ash Utilization Conference[C].Shanghai,China,1991:10--12. 被引量:1
  • 6SORONSHIAN P,ALHOZAIMY A.Correlation between strength and permeability of fly ash concrete[A]//10th International Ash Use Symposium[C].Orlando,Florida,USA,1993:10-12. 被引量:1
  • 7ZHANG M H,GJφRV O E.Penetration of cement paste into lightweight aggregate[J].Cem Concr Res,1991,22(1):47-55. 被引量:1
  • 8SARKAR S.L,CHANDRA S,BERNTSSON L.Interdependence of microstructure and strength of structural lightweight aggregate concrete[J].Cem Concr Compos,1992,14(3):239-248. 被引量:1
  • 9SCRIVENER K L,BENTUR A,PRATT P L.Quantitative characterization of the transition zone in high strength concretes[J].Adv Cem Res,1988,1(4):230-237. 被引量:1
  • 10ZHANG M H,GJφRV O E.Microstruchture and the interfacial zone between lightweight aggregate and cement paste[J].Cem Concr Res,1990,20(4):610-618. 被引量:1

共引文献84

同被引文献22

  • 1石彩虹,李学军.425^#水泥在C40、C50级高强度泵送砼中的研究与应用[J].内蒙古科技与经济,2004(24):55-56. 被引量:1
  • 2胡曙光,王发洲,丁庆军.轻集料与水泥石的界面结构[J].硅酸盐学报,2005,33(6):713-717. 被引量:42
  • 3孙海林,叶列平,丁建彤,郭玉顺.高强轻骨料混凝土收缩和徐变试验[J].清华大学学报:自然科学版,2007,47(6):765-767. 被引量:21
  • 4JORGE L F,SCHANZLIN J,LOPES S M R, et al.Time-de- pendent behaviour of timber lightweight concrete composite floors[J]. Engineering Structures, 2010,32(12) : 3966-3973. 被引量:1
  • 5ZHUANG Yizhou, CHEN Caiyi, JI Tao. Effect of shale ceram- site type on the tensile creep of lightweight aggregate concrete [J].Construetion and Building Materials,2013,46 : 13-18. 被引量:1
  • 6LOPEZ M,KAHN L F, KURTIS K E.Characterization of e- lastic and time-dependent deformations in high performance lightweight concrete by image analysis [J]. Cement and Concrete Research, 2009,39(7) : 610-619. 被引量:1
  • 7de SCHUTTER G. Fundamental study of early age concrete behaviour as a basis for durable concrete structures[J].Mate- rials and Structures, 2002,34(245) : 15-21. 被引量:1
  • 8JIANG Wei,de SCHUTTER G, YUAN Yong.Degree of hy- dration based prediction of early age basic creep and creep re- covery of blended concrete[J].Cement and Concrete Compos- ites, 2014,48 : 83-90. 被引量:1
  • 9UY B, DAS S. Time effects in concrete filled steel box columns in tall buildings[J]. The Structural Design of Tall Buildings, 1997,6 (1) : 1-22. 被引量:1
  • 10JIANG Wei, GONG Jian, de SCHUTTER G, et al. Time-de- pendent analysis during construction of concrete-tube for tower high-rise building[J].Structural Concrete, 2012,13 (4) : 236-247. 被引量:1

引证文献6

二级引证文献1

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈