复合骨料混凝土力学与干缩性能试验研究 预览 被引量:2

Experimental study on mechanical properties and dry-shrinkage of concrete mixed with composite coarse-aggregate
在线阅读 下载PDF
收藏 分享 导出
摘要 研究了轻骨料粒径混合比例、轻骨料等体积替代碎石比例对复合骨料混凝土基本力学性能和干缩性能的影响,轻骨料粒径10~16mm和16~20mm的混合比例分别取5:5(LA1)、7:3(LA2)和3:7(LA3),轻骨料等体积替代碎石比例分别取10%、20%和30%。结果表明:采用LA2替代比例为10%和20%时,可获得强度高于普通混凝土而弹性模量低于普通混凝土的复合骨料混凝土;采用LAl和LA3替代比例为10%和20%时,复合骨料混凝土的抗拉强度明显降低;当轻骨料混合比例相同而增大轻骨料替代率时,复合骨料的强度和弹性模量均呈现降低的趋势;特别是当采用LA3替代率为30%时,复合骨料混凝土的抗压、抗拉和弹性模量均低于普通混凝土;复合骨料混凝土的早龄期干缩随着轻骨料替代比例的增加而显著减小。 Tests were carried out to study effects of the grain composite ratio in different sizes and lightweight aggregate replacing ratio for crushed stone by equal volume on the basic mechanical properties and dry-shrinkage of concrete mixed with composite coarse-aggregate (CCAC),in which the grain composite ratios in size of 10-16 mm to 16-20 mm were taken as 5:5 (LA1),7:3 (LA2)and 3:7(LA3);the lightweight aggregate replacing ratios for crushed stone by equal volume were taken as 10%, 20% and 30%.The results show that: the CACC could be obtained in higher strength and lower elastic modulus than ordinary concrete while LA2 was used with replacing ratio of 10% and 20%,the tensile strength of CACC decreased obviously while LA1 and LA3 was used with replacing ratio of 10% and 20% ,the strength and modulus of CACC were in decrease tendency while lightweight aggregate replacing ratio increased in same grain composite ratio, all the compressive and tensile strengths as well as elastic modulus of CACC were lower than those of ordinary concrete while LA3 was used with replacing ratio of 30%, the early-age dry-shrinkage of CACC reduced remarkably with the increasing lightweight aggregate replacing ratio.
作者 李凤兰 郭克宁 李静 LI Feng-lan , GUO Ke-ning, LI Jing ( 1. School of Civil Engineering and Communication,North China Institute of Water Conservancy and Hydroelectric Power, Zhengzhou 450011, China; 2. Hebei Provincial Second Investigation, Design and Research Institute of Water Conservancy and Hydroelectric Power, Shijiazhuang 050021, China)
出处 《混凝土》 CAS CSCD 北大核心 2011年第10期 28-30,共3页 Concrete
基金 郑州市科技领军人才资助项目(096SYJH23105) 河南省教育厅自然科学研究计划项目(2010A560011)
关键词 混凝土 复合骨料 轻骨料 内养护 粒径混合比 轻骨料替代率 力学性能 干缩 concrete composite coarse-aggregate lightweight aggregate internal curing grain composite ratio in different sizes lightweightaggregate replacing ratio mechanical properties dry-shrinkage
作者简介 李凤兰(1964-),女,教授,主要从事土木工程材料研究。 联系地址:河南省郑州市北环路36号华北水利水电学院土木与交通学院(450011) 联系电话:0371-69127373
  • 相关文献

参考文献15

二级参考文献23

  • 1Kenneth W. Meeks, Nicholas J. Carino, Curing of High - Performance Concrete, United states Department of Commerce Technology Administration, second printing, 2002. 被引量:1
  • 2D P Bentz, K A Snyder, Protected Paste Volume in Concrete: Extension to Internal Curing Using Saturated Lightweight Fine Aggregate, Cement and Concrete Research, Vol.29(11), 1863- 1867,1999. 被引量:1
  • 3Mette Geiker et al, Mitigating Autogenons Shrinkage by Internal Curing,American Concrete Institute Fall Convention, High Performance Structural Lightweight Concrete and Internal Curing and Enhanced Hydration, October(2002). 被引量:1
  • 4Salah A. Altoubat, David A. Langue, Early Age Stresses and Creep -shrinkage Interaction of Restrained Concrete, Civil Engineering Studies,report No. 14, March 2001. 被引量:1
  • 5David W.Mokarem, Development of Concrete Shrinkage Performance Specifications, Virginia Transportation Research Council, May 1, 2002. 被引量:1
  • 6High Performance Concrete: Low Shrinkage Concrete. 被引量:1
  • 7ZHANG Minhong, GJORV O E.Microstructure of the interfacial zone between LWA and cement paste[J].Cem Concr Res,1990,20(4):613-614. 被引量:1
  • 8ZHANG Minhong, GJORV O E.Penetration of cement paste into lightweight aggregate[J].Cem Concr Res,1992,22(1):47-55. 被引量:1
  • 9LO Y, GAO X F, JEARY A P. Microstructure of pre-wetted aggregate on lightweight concrete[J].Build Environ,1999,34:759-764. 被引量:1
  • 10HU Shuguang, LI Yue. Research on the hydration,hardening mechanism,and microstructure of high performance expansive concrete[J].Cem Concr Res,1999,29(8):1 013-1 016. 被引量:1

共引文献129

同被引文献37

引证文献2

二级引证文献5

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈
新型冠状病毒肺炎防控与诊疗专栏